残余应力作用下脆性膜/基材料的断裂行为

假定膜内的残余拉应力足以使膜发生开裂,利用膜/基材料中含弹性界面层的剪滞模型,研究了脆性膜/基材料在残余应力作用下的开裂行为特征,探讨了膜内正应力、膜/基界面切应力的分布规律,获得了膜的裂纹密度与残余应力大小之间的解析表达式。在裂纹密度、材料的力学和几何参数确定的情况下,该解析表达式可以用来评估残余应力的大小。最后,分析了膜的裂纹密度与残余应力、膜的厚度、弹性模量、断裂强度以及界面层的切变模量之间的内在关联,绘出了这些参数影响膜裂纹密度的变化曲线。     

平头弹丸侵彻金属靶板的数值仿真

基于ABAQUS/Explicit非线性有限元分析程序,通过二次开发利用含损伤的Johnson-Cook本构模拟靶板材料,对刚性平头弹丸垂直侵彻不同厚度的金属靶板进行了数值仿真,实现了侵彻过程的可视化。结果表明：网格密度对计算结果有影响,但随着网格密度增加,结果趋于收敛;侵彻过程中,弹丸与靶板发生了多次碰撞,靶板的塑性变形局限在很窄的剪切带内;对数值计算结果与试验结果进行了比较,发现二者吻合得较好。相关结论对防护结构的设计具有指导意义。     

22SiMn2TiB装甲钢异种焊接接头超声波探伤探头设计

用常规探头对22SiMn2TiB装甲钢与TWE312异种钢焊接接头进行缺陷检测,杂波和伪缺陷波导致灵敏度、信噪比不高。用扫描电镜观察到这种异种钢焊接接头主要为奥氏体+铁素体组织,其中奥氏体是主体组织。根据焊缝的组织特点,设计出了2.5P13×13K1.5型专用探头。在预制缺陷的焊接接头上进行了验证试验,结果表明2.5P13×13K1.5探头对接头内部的缺陷具有较高的检出率。     

新型直升机旋翼系统减摆阻尼器动态性能研究

参照某型直升机旋翼系统对减摆阻尼器的结构及性能的要求,首次研制了一种金属橡胶-钢丝绳索型减摆器。通过粘弹等效阻尼测试,结果表明这种减摆器能满足技术指标要求,且具有减振效果更优、性能更稳定和环境适应能力更强等优点,为直升机旋翼系统减摆器的设计与制造提供了一种新技术思路。     

一种遥测信号的模式识别算法研究

如何进行遥测信号的提取是遥测信号数据处理的重要环节,针对典型脉冲码元,提出了特征提取和软件模板的建立及算法的实现.     

建立一类挠性航天器的动力学模型及面向控制的仿真环境

对于一类具有一个中心刚体和两块对称安装的太阳帆板的挠性航天器,针对其帆板较长、弹性位移较大,导致根据文献[2]直接建立的模型不准的问题,提出将弹性帆板分段处理的方法,分别引入浮动坐标系,建立系统的动力学仿真模型。并将针对整体模型设计的控制规律作用于该模型,进行了数值仿真。仿真结果表明,对于大变形情况,分段处理的方法十分有效。     

钢筋混凝土外粘钢板结构裂缝的有限元数值模拟

随着高技术武器的不断发展,防护工程正面临着前所未有的威胁和挑战,新型防护结构及材料已经成为研究的热点。针对这一实际背景,运用ANSYS大型有限元软件,采用数值模拟的方法对普通钢筋混凝土结构和外粘钢板混凝土结构在相同均布面荷载作用下的变形、钢筋应力以及结构裂缝的开展情况进行了比较。结果表明外粘钢板的钢筋混凝土结构能够大大增强结构的抗力,并且有效的抑制了裂缝的开展。     

Experimental investigation on anti-penetration performance of polyurea-coated ASTM1045 steel plate subjected to projectile impact

In this study, the anti-penetration performance of polyurea/ASTM1405-steel composite plate subjected to high velocity projectile was analyzed. Two kinds of modified polyurea material (AMMT-053 and AMMT-055) were selected and a ballistic impact testing system including speed measuring target system and high-speed camera was designed. This experiment was conducted with a rifle and 5.8 mm projectile to explore the effects by the polyurea coating thickness, the polyurea coating position and the glass-fiber cloth on the anti-penetration performance of polyurea/ASTM1405-steel composite plate. The result showed that the effects of polyurea coating position were different between two types of polyurea, and that the effects of glass-fiber position were disparate between two types of polyurea as well. For AMMT-053 polyurea material, it was better to be on front face than on rear face; whereas for AMMT-055 pol-yurea, it was better to be on rear surface although the difference was very subtle. Additionally, formulas had been given to describe the relationship between the effectiveness of polyurea and the thickness of polyurea coating. In general, AMMT-055 had better anti-penetration performance than AMMT-053. Furthermore, five typical damage modes including self-healing, crack, local bulge, spallation and local fragmentation were defined and the failure mechanism was analyzed with the results of SHPB test. Additionally, the bonding strength played an important role in the anti-penetration performance of polyurea/steel composite plate.     

太赫兹粗糙金属目标镜面雷达散射截面预估方法

在太赫兹频段,研究金属目标表面粗糙度对雷达散射截面(Radar Cross Section,RCS)的调制作用,对粗糙金属目标的RCS缩比测量具有重要意义.通过研究太赫兹粗糙金属目标镜面RCS随粗糙度的变化规律,结合相干、非相干散射理论,在基尔霍夫近似法的基础上,提出一种特定参数区间粗糙金属目标镜面RCS的预估方法,并...     

ITO及WO3在电解液中的交流阻抗特性

采用表面过程法拉第阻纳表达式方法与等效电路方法,研究透明ITO平面电极及带WO3薄膜层的ITO平面电极处于1 mol LiClO4丙烯碳酸酯电解液中的电化学阻抗谱.分析显示WO3薄膜层有效地阻止了表面吸附参量对ITO电极反应的影响,使电极反应仅受电极电位的影响,并且随WO3薄膜在电解液中浸泡时间的增加,WO3薄膜的常相位角元件的特性最终回归为电容效应.